X – Y – Z = 15 x 13 x 18 in
(381 x 330 x 460 mm)
DuraForm ProX PA
0.003 – 0.006 in (0.08 – 0.15 mm) (0.004 in, 0.10 mm)
1.8 l/hr
General Properties |
|||||
Measurement |
Condition |
Metric |
U.S. |
||
Sintered Part Density |
Internal |
0.95 g/cm3 |
0.95 g/cm3 |
||
Mechanical Properties |
|||||
Measurement |
Condition |
Metric |
U.S. |
||
Tensile Strength, Ultimate |
D638 |
47 MPa |
6527 psi |
||
Tensile Strength, Break |
D638 |
45 MPa |
6817 psi |
||
Tensile Modulus |
D638 |
1770 MPa |
257 ksi |
||
Elongation at Yield |
D638 |
14 % |
14 % |
||
Elongation at Break |
D638 |
22 % |
22 % |
||
Flexural Strength |
D790 |
63 MPa |
9137 psi |
||
Flexural Modulus |
D790 |
1650 MPa |
239 psi |
||
Hardness, Shore D |
D2240 |
73 |
73 |
||
Impact Strength (notched Izod, 23 °C) @0.12” |
D256 |
45 J/m |
0.84 ft-lb/in |
||
Impact Strength (unnotched Izod, 23 °C) @0.12” |
D256 |
644 J/m |
12.1 ft-lb/in |
||
Thermal Properties |
|||||
Measurement |
Condition |
Metric |
U.S. |
||
HDT @ 0.45 MPa |
D648 |
182 °C |
360 °F |
||
HDT @ 1.82 MPa |
D648 |
97 °C |
207 °F |
||
Coefficient of Thermal Expansion (0-50 °C) |
E831 |
109.5 μm/m-°C |
109.5 μm/m-°C |
||
Coefficient of Thermal Expansion (85-145 °C) |
E831 |
221.7 μm/m-°C |
221.7 μm/m-°C |
||
Specific Heat Capacity |
E1269 |
1.55 J/g-°C |
1.55 J/g-°C |
||
Thermal Conductivity |
E1530 |
0.21 W/m-K |
0.21 W/m-K |
||
Flammability 3.0 mm |
UL94 |
HB |
HB |
||
Electrical Properties |
|||||
Measurement |
Condition |
Metric |
U.S. |
||
Volume Resistivity |
D257 |
1.46 x 1015 Ω . cm |
1.46 x 1015 Ω . cm |
||
Surface Resistivity |
D257 |
4.66 x 1015 Ω |
4.66 x 1015 Ω |
||
Dissipation Factor, 1 KHz |
D150 |
0.022 |
0.022 |
||
Dielectric Constant, 1 KHz |
D150 |
2.85 |
2.85 |
||
Dielectric Strength |
D149 |
15.2 kV/mm |
386 kV/in |